Download Dy - Er … Ir - Y: Supplement to Subvolumes IV/5B, IV/5C and by B. Predel (auth.), B. Predel (eds.) PDF

By B. Predel (auth.), B. Predel (eds.)

Volume 12 of crew IV provides part diagrams, crystallographic and thermodynamic facts of binary alloy structures. The subvolume C includes platforms from Dy-Er...Ir-Y. quantity 12 types a complement to quantity 5.

Show description

Read Online or Download Dy - Er … Ir - Y: Supplement to Subvolumes IV/5B, IV/5C and IV/5D PDF

Similar nonfiction_12 books

Surface Modification Technologies XIII: Proceedings of a conference held in Singapore, 7-10 October 1999

The forty six papers provided at this occasion disguise not easy fabrics, Lasers and floor Melting, Electrodeposition and evaluate of changed Surfaces, Thermal Spray thoughts, Nitride Coatings and assessment of transformed Surfaces.

Additional info for Dy - Er … Ir - Y: Supplement to Subvolumes IV/5B, IV/5C and IV/5D

Sample text

Trans. A. : J. Less-Common Met. : Z. Metallkde. : J. Alloys Comp. : J. Phase Equil. 1007/978-3-642-24778-1_18 © Springer-Verlag Berlin Heidelberg 2013 Phase Equilibria, Crystallographic and Thermodynamic Data of Binary Alloys 40 Er - Pd (Erbium - Palladium) Phase diagram Using the CALPHAD method Du et al. [00 Du] have calculated the phase diagram. The result obtained is given in Fig. 1. In Fig. 2 the middle part is shown in an enlarged version. Thermodynamics Standard enthalpies of formation have been determined by Guo et al.

For Figs. 1 and 2 temperatures for special reactions were taken from a table given by [00 Du]. The coincidence between figure and table, however, is not always good. Thermodynamics [00 Du] have calculated the enthalpies of formation for intermediate phases, too. The data obtained are plotted in Fig. 3. On the basis of high-temperature calorimetry Guo et al. [96 Guo] have determined standard enthalpies of formation of intermediate phases at 1474 K. The results are given in Table 1. Table 1. Dy-Pd.

00 Du] have calculated the phase diagram by means of the CALPHAD technique. The results are shown in Fig. 1. The Pd-rich part is reproduced in Fig. 2 in an enlarged version. It should be pointed out that the informations for drawings Fig. 1 and Fig. 2 have been taken from figures in [00 Du]. But no data concerning temperatures have been given there. For Figs. 1 and 2 temperatures for special reactions were taken from a table given by [00 Du]. The coincidence between figure and table, however, is not always good.